S500MC plate zero cut are cost effective

After quenching and tempering, the 40Cr alloy steel plate has good comprehensive mechanical properties, good low-temperature impact toughness and low notch sensitivity. The hardenability of steel is good. It can be hardened to Ф28～60mm in water quenching

After quenching and tempering, the 40Cr alloy steel plate has good comprehensive mechanical properties, good low-temperature impact toughness and low notch sensitivity. The hardenability of steel is good. It can be hardened to Ф28～60mm in water quenching and Ф15～40mm in oil quenching. In addition to quenching and tempering, 40cr sheet is also suitable for cyanidation and high-frequency quenching.

In production and operation, the company always attaches great importance to product S500MC plate zero cut quality. Product quality is stable, performance index is superior, after-sales service is in place, the company's products have been exported to the United States, Southeast Asia, Africa, the Middle East and other countries and regions, occupying a large part of the overseas market S500MC plate zero cut. And a large number of famous enterprises at home and abroad have formed a solid strategic partnership with the company.

The hot rolling method is to heat the S500MC plate zero cut steel material to about 1000 ℃ ~ 1250 ℃ and use the rolling mill to roll it. The traditional hot rolling process is generally divided into the following two steps: the first step is to use the primary rolling mill or billet rolling mill to roll the ingot, billet or continuous casting billet into a certain shape and size of billet. This kind of S500MC plate zero cut rolling process is usually called semi-finished product production, also called blank production.

S500MC plate zero cut, Q345B low alloy steel plate composition:
1) Low carbon: Due to the high requirements for toughness, weldability and cold forming properties, its carbon content does not exceed 0.20%;
2) Add manganese-based alloying elements;
3) Adding auxiliary elements such as niobium, titanium or vanadium: a small amount of niobium, titanium or vanadium forms fine carbides or carbonitrides in the Q345B steel, which is conducive to obtaining fine ferrite grains and improving the strength and toughness of the steel;
In addition, adding a small amount of copper (≤0.4%) and phosphorus (about 0.1%) can improve the corrosion resistance. Adding a small amount of rare earth elements can desulfurize and degas, purify steel, improve toughness and process performance.

Compared with other fast-moving consumer goods, steel consumption is obviously different, with a wide range of use and a long service life. Therefore, the quality and service of steel materials are particularly important. Service is always one of our top concerns, especially after-sales service. We have mature after-sales service team, and can help you solve problems professionally during application of the steel materials.