Q355NH material is a Chinese steel grade to GB/T 4171-2008 atmospheric corrosion resisting structural steel. There are five steel levels under Q355NH: Grade A, B, C, D, and E. Q355NH structural steel sheet is mainly used in vehicles, containers, construct

Q355NH material is a Chinese steel grade to GB/T 4171-2008 atmospheric corrosion resisting structural steel. There are five steel levels under Q355NH: Grade A, B, C, D, and E. Q355NH structural steel sheet is mainly used in vehicles, containers, construction, towers or other structural parts and other structures. It has good resistance to atmospheric corrosion. We supply 1.0982 thermomechanically rolled steels, Q355NH steel plates thickness less than 120mm.

Based on the principle of win-win and mutual benefit, the company operates in good faith, strictly controls the quality, and provides perfect after-sales service, which has won unanimous praise. The success of the company is not only the 1.0982 thermomechanically rolled steels hard work and wisdom of the company's employees, but also the deep love of the majority of consumers. It also inspires all employees of the company to have the courage to strive. We will continue to innovate and leap forward, create greater brilliance of the enterprise, and make our own contribution to the development of the 1.0982 thermomechanically rolled steels steel industry.

X-rays or γ-rays are projected on the surface of the steel plate, and rubber can be placed on the other side of the steel plate. Since the radiation propagates through the steel plate and is absorbed, the intensity is different due to the presence or absence of defects, so the film can record the shape and position of the defects. This 1.0982 thermomechanically rolled steels method is sensitive to the detection of common steel plate defects such as slag inclusions, porosity and pores. The disadvantage is that it is difficult to find the specific depth of the defect and it is not easy to find cracks.

When phosphorus, copper, chromium, nickel and other trace elements are added to the weathering steel sheet, a dense and strong adhesion protective film will be formed on the steel surface, which will hinder the corrosion from spreading and developing inside, and protect the substrate under the rust layer, so as to slow down the corrosion rate. That is why the weathering steel sheet, 1.0982 thermomechanically rolled steels has good atmosphere corrosion resistance.

After the order is finished, our after-sales service center will send an email to make a feedback about our steel products' quality. We have phone service every three months to remind our customers of the possible problems and collect advices or suggestions in quality and service. Upon the collection of advices or suggestions, our after-sales service will quickly make technical solutions to wipe out the customer problem.